大直径高质量太阳能级硅单晶磁场直拉技术研究
吴明明，王建臣
（衢州学院，浙江 衢州 324000）
摘要：直拉法易于制备大直径单晶，但在其拉制过程中，晶体生长系统中的熔体会产生自然对流、毛细对流以及强迫对流。在上述三种熔体对流的相互作用下，会使晶体中的氧、碳等杂质产生不均匀分布而影响晶体质量。通过在熔体空间中引入磁场可以有效抑制熔体各种对流，应用于硅单晶生长系统的磁场有横向磁场、纵向磁场和勾形磁场，其中勾形磁场在控制大直径硅单晶中的氧等杂质的含量以及径向分布均匀性方面效果较好。
关键词：直拉硅单晶；大直径；高质量；熔体对流；均匀性；磁场
中图分类号：TM914.4+1 文献标志码：A 文章编号：1006－0316 (2013) 11－0077－04
The research of magnetic field Czochralski technology of large diameter and high quality solar grade single crystal silicon
WU Ming-ming，WANG Jian-chen
( Quzhou University, Quzhou 324000, China )
Abstract：Czochralski method is easy to pull large diameter single crystal, but in its pulling process, the melt of crystal growth system will produce natural convection, Marangoni convection and forced convection. Under the interactions of the three types of melt convection, it will make uneven distribution of oxygen, carbon and other impurities which will affect crystal quality. It can effectively suppress all kinds of melt convections through the introduction of the magnetic field. There is transverse magnetic field, the longitudinal magnetic field or cusp magnetic field applied to silicon single crystal growth system. Cusp magnetic field is more effective to control oxygen and other impurities’ content and uniformity of the radial distribution of large diameter silicon single crystal.
Key words：CZ Si crystal；large-diameter；high quality；melt convection；uniformity；magnetic field
———————————————
收稿日期：2013－05－21
基金项目：2011年衢州市科技计划项目《大直径高质量太阳能级硅单晶磁场直拉技术研究》（20111041）
作者简介：吴明明（1971－），女，浙江桐庐人，博士研究生，副教授，高级工程师，主要研究方向为功能材料精密加工。
- 上一篇：一种新型灌装用控制阀的设计与应用
设为首页 | 加入收藏 | 免责条款
《机械》杂志版权所有 Copyright©2008-2012 Jixiezazhi.com All Rights Reserved
电话：028-85925070 传真：028-85925073 E-mail：jixie@vip.163.com
地址：四川省成都锦江工业开发区墨香路48号 邮编：610063
Powered by PageAdmin CMS