中压主汽门阀盖螺栓断裂原因分析

 石彩华

(苏州健雄职业技术学院 机电工程系,江苏 太仓 215411)
摘要:中压主气门阀盖螺栓在运转两年后出现多根断裂,通过观察和分析20Cr1Mo1VnbTiB高温螺栓断口的宏观及微观形貌,检验化学成分、测试力学性能,显微组织检验等方法,分析螺栓断裂原因。力学性能和化学成分符合要求,但螺纹根部粗糙度比较大,硬度为316 HBW2.5/187.5超过标准中规定的硬度252~302 HBW上限值,金相组织是回火索氏体。分析结果表明,螺纹根部粗糙,引起局部应力集中,金相组织不符合要求,硬度超过标准中的规定,晶粒粗大等是螺栓断裂的主要原因。在生产中,要加强高温紧固件性能检测,遵守拆装要求,定期喷涂防腐介质,以防此类事故发生。
关键词:中压主汽门;高温螺栓;断裂;金相组织
中图分类号:TG111.91 文献标志码:B doi:10.3969/j.issn.1006-0316.2014.10.017
文章编号:1006-0316 (2014) 10-0074-03
Fracture analysis of the bolt on the RSV bonnet
SHI Cai-hua
( Department of Electrical and Mechanical Engineering, Suzhou Chien-Shiung Institute of Technology, Taicang 215411, China )
Abstract:Many bolts on the RSV bonnet are broken after two years work Through the macro and micro-analysis of the thread tooth surface and fracture, chemical compositions examination, mechanical properties test, microstructure exam-nation etc, the fracture of 20Cr1Mo1VnbTiB high temperature bolts is analyzed. Chemical composition and mechanical properties of bolt meet standards, but local stress concentration by rough machined is found, 316HBW2.5/187.5 hardness exceeds the upper limits of the standard hardness (252 ~ 302HBW), the microstructure is tempered sorbite. The results show that main reasons caused fracture is Local stress concentration by rough machined, coarsening grain, excessive hardness, incorrect bolt Metallographic microstructure etc. In production, the high temperature bolts performance testing is strengthened, the requirements of assembly and disassembly requirements is complied; the anti-corrosion medium is regular sprayed to prevent such occurrences.
Key words:RSV;high temperature bolts;fracture;metallographic microstructure
———————————————
收稿日期:2014-04-22
基金项目:江苏省国际科技合作计划项目:中德精密机械部件制造国际技术转移中心(201369334)
作者简介:石彩华(1980-),女,山东东明人,硕士研究生,工程师,讲师,主要从事机械产品的设计与缺陷检测的工作。
 

 

设为首页  |  加入收藏    |   免责条款
《机械》杂志版权所有     Copyright©2008-2012 Jixiezazhi.com All Rights Reserved 

  电话:028-85925070    传真:028-85925073    E-mail:jixie@vip.163.com

地址:四川省成都锦江工业开发区墨香路48号   邮编:610063

蜀ICP备08103512号

Powered by PageAdmin CMS